The effect of mean pore size on cell attachment, proliferation and migration in collagen glycosaminoglycan scaffolds for tissue engineering.

Download (2.55 MB)
journal contribution
posted on 22.11.2019 by Ciara M. Murphy, Matthew G. Haugh, Fergal J. O'Brien
In the literature there are conflicting reports on the optimal scaffold mean pore size required for successful bone tissue engineering. This study set out to investigate the effect of mean pore size, in a series of collagen-glycosaminoglycan (CG) scaffolds with mean pore sizes ranging from 85 microm to 325 microm, on osteoblast adhesion and early stage proliferation up to 7 days post-seeding. The results show that cell number was highest in scaffolds with the largest pore size of 325 microm. However, an early additional peak in cell number was also seen in scaffolds with a mean pore size of 120 microm at time points up to 48 h post-seeding. This is consistent with previous studies from our laboratory which suggest that scaffold specific surface area plays an important role on initial cell adhesion. This early peak disappears following cell proliferation indicating that while specific surface area may be important for initial cell adhesion, improved cell migration provided by scaffolds with pores above 300 microm overcomes this effect. An added advantage of the larger pores is a reduction in cell aggregations that develop along the edges of the scaffolds. Ultimately scaffolds with a mean pore size of 325 microm were deemed optimal for bone tissue engineering.

History

Comments

This article is also available at http://www.sciencedirect.com/

Published Citation

Murphy CM, Haugh MG, O'Brien FJ. The effect of mean pore size on cell attachment, proliferation and migration in collagen-glycosaminoglycan scaffolds for tissue engineering. Biomaterials. 2010;31(3):461-6.

Publication Date

01/01/2010

Publisher

Butterworth-Heinemann In Association With The Biological Engineering Society

PubMed ID

19819008

Exports